活性剂对厚壁管TIG焊接的影响
Effect of Active Agent on TIG Welding of Thick-walled Pipe
- 2024年54卷第1期 页码:107-113
DOI: 10.7512/j.issn.1001-2303.2024.01.17
扫 描 看 全 文
扫 描 看 全 文
李佳伟,陈炫如,黄泽,等.活性剂对厚壁管TIG焊接的影响[J].电焊机,2024,54(1):107-113.
LI Jiawei, CHEN Xuanru, HUANG Ze, et al.Effect of Active Agent on TIG Welding of Thick-walled Pipe[J].Electric Welding Machine, 2024, 54(1): 107-113.
TIG焊接焊缝质量高但其熔深小,生产率低。若在被焊工件表面涂敷一层特殊的活性剂,再进行TIG焊接,能够起到增大熔深的效果,即A-TIG焊。研究了三种不同活性剂对,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483813&type=,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483821&type=,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483817&type=,2.26000023,2.50898361,3.175,54 mm×8 mm厚的20#钢厚壁管TIG焊接的影响,研究发现:添加3号活性剂的接头外观质量最好,添加2号活性剂的次之,添加1号活性剂的最差;三种活性剂熔深均大于8 mm,熔深增加量均达到3.211 mm以上,而不添加活性剂的厚壁管则不能焊透。使用2号活性剂增加焊接熔深的效果最明显。20#钢管母材显微组织是铁素体和珠光体,接头热影响区组织相较于母材更粗大,焊缝区的晶粒进一步长大,在原奥氏体晶界处产生针状粗大的先共析铁素体,主要组织仍为珠光体和铁素体混合物。添加三种活性剂的焊缝组织无明显变化,获得的焊接接头拉伸试样均断裂在母材,焊缝强度均高于母材。
TIG welding common welding consumables produces high quality welds and beautiful weld shapes. However, when welding thicker plates and pipes, the welding penetration is small and the welding productivity is low. Coating a layer of special active agent on the surface of the workpiece to be welded for TIG welding can increase the penetration depth and reduce the penetration width, which is the so-called A-TIG welding. This paper studies the influence of three different active agents on the TIG welding of a 20# steel thick-walled pipe with a thickness of ,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483826&type=,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483833&type=,https://html.publish.founderss.cn/rc-pub/api/common/picture?pictureId=53483829&type=,2.00000000,2.22033930,3.175,54 mm×8 mm. The results showed that the appearance quality of the joint with No. 3 active agent was the best, followed by No. 2 active agent, and the worst with No. 1 active agent. The penetration depths of the three active agents are all greater than 8 mm, and the penetration depth increases are all above 3.211 mm. Thick-walled pipes without active agent cannot be welded through. For the samples welded with No. 2 active flux, the average width of the front side of the weld is 8.639 mm and the average width of the back side is 7.621 mm. The effect of increasing the penetration depth is the most obvious. The microstructure of 20# steel pipe base metal is ferrite and pearlite. The structure of the heat-affected zone of the joint is larger than that of the base metal, and the grains in the weld zone are further grown. At the austenite grain boundary, acicular coarse proeutectoid ferrite is produced, and the main structure is still a mixture of pearlite and ferrite, and a small amount of upper bainite and lath martensite. The tensile specimens with three active agents all fractured on the base material, and the weld strength was higher than that of the base material.
活性剂TIG焊熔深显微组织力学性能
active agentTIG weldingpenetrationmicrostructuremechanical properties
刘自刚,周晓静,朱婷婷,等. A-TIG焊接方法研究现状及展望[J]. 材料导报, 2021,35(S2):353-357.
LIU Z G,ZHOU X J,ZHU T T,et al. Research Status and Prospect of A-TIG Welding Method[J]. Materials Reports, 2021,35(S2):353-357.
李春凯,席保龙,石玗,等. 氟化物活性TIG焊电弧特征的光谱分析[J]. 焊接学报, 2021,42(08):54-58.
LI C K,XI B L,SHI Y,et al. Spectral analysis of A-TIG welding arc with fluorides activating flux[J]. Transactions of The China Welding Institution, 2021,42(08):54-58.
朱嘉文,李佳,杨成刚,等. 活性剂对铁素体不锈钢A-TIG接头熔深及组织性能研究[J]. 精密成形工程, 2022,14(10):105-112.
ZHU J W,LI J,YANG C G,et al. Study on Penetration Depth and Microstructure Properties of Ferritic Stainless Steel A-TIG Welding Joint[J]. Journal of Netshape Forming Engineering, 2022,14(10):105-112.
赵忠义, 伏金生, 李 飞,等.不锈钢 A- TIG 焊接方法[J]. 电焊机,2008, 38(2): 67-68.
ZHAO Z Y,FU J S,LI F,et al. Welding method of A-TIG for stainless steel[J]. Electric Welding Machine,2008, 38(2): 67-68.
杨成刚,任泽良,宋友民,等. 奥氏体不锈钢A-TIG焊工艺研究[J]. 精密成形工程, 2019,11(5): 50-54.
YANG C G,REN Z L,SONG Y M,et al. A-TIG Welding Technology of Austenitic Stainless Steel[J]. Journal of Netshape Forming Engineering, 2019,11(5): 50-54.
张瑞华, 樊丁, 余淑荣. 低碳钢A-TIG焊的活性剂研制[J]. 焊接学报, 2003, 24(2): 16-18.
ZHANG R H,FAN D,YU S R. Study activating flux for mild steel[J]. Transactions of The China Welding Institution, 2003, 24(2): 16-18.
张瑞华, 樊丁. 低碳钢A-TIG焊的活性剂的焊接性研究[J]. 甘肃工业大学学报, 2003, 29(1): 19-21.
ZHANG R H,FAN D. Study of weldability of activating flux for A-TIG welding of mild steel[J]. Journal of Gansu University of Technology, 2003, 29(1): 19-21.
赵勇, 严铿. 不锈钢A-TIG焊活性剂对焊缝成形的影响[J]. 焊接技术, 2004, 33(4): 24-25.
ZHAO Y,YAN Q. Effect of active flux on figuration of weld in A-TIG welding of stainless steel[J]. Welding Technology, 2004, 33(4): 24-25.
刘黎明, 张兆栋, 沈勇, 等. 活性剂对镁合金TIG焊接熔深的影响[J]. 金属学报, 2005, 42(4): 399-404.
LIU L M,ZHANG Z D,SHEN Y,et al. Effects of Activating Fluxes on TIG Welding Penetration of Magnesium Alloy[J]. Acta Metallurgica Sinica, 2005, 42(4): 399-404.
Kulkarn A, Dwivedi D K, Vasudevan M. Microstructure and mechanical properties of A-TIG welded AISI 316L SS-Alloy 800 dissimilar metal joint[J]. Materials Science & Engineering A, 2020,790:139685.
刘文月,任毅,王爽,等.钢中奥氏体晶粒长大规律[J].上海金属, 2019,41(4): 88-93.
LIU W Y,REN Y,WANG S,et al. Austenite Grain Growth Behavior in Steels[J]. Shanghai Metals, 2019,41(4): 88-93.
相关作者
相关机构