工艺参数对高强钢窄间隙激光填丝焊鼓胀区影响
Influence of Process Parameters on Bulging Region of High Strength Steel in Narrow Gap Laser Welding with Wire Filler
- 2022年52卷第10期 页码:107-113
DOI: 10.7512/j.issn.1001-2303.2022.10.16
扫 描 看 全 文
扫 描 看 全 文
韩鹏薄,黄瑞生,孙静涛,等.工艺参数对高强钢窄间隙激光填丝焊鼓胀区影响[J].电焊机,2022,52(10):107-113.
HAN Pengbo, HUANG Ruisheng, SUN Jingtao, et al.Influence of Process Parameters on Bulging Region of High Strength Steel in Narrow Gap Laser Welding with Wire Filler[J].Electric Welding Machine, 2022, 52(10): 107-113.
研究了主要工艺参数对高强钢窄间隙激光填丝焊鼓胀区的影响。通过测量不同工艺条件下焊缝鼓胀区的宽度,W,max,及其距焊缝表面的距离,d,,建立了主要焊接参数与鼓胀区尺寸之间的关系。研究结果表明焊丝与母材吸收能量的比例大小是影响鼓胀区宽度及位置主要因素,减小激光功率、增加焊速和送丝速度能够减小鼓胀区。进一步提出了不同鼓胀角,β,<30°与,β,>60°的工艺区间,并且减小鼓胀角,β,是获得大深宽比条件下无凝固裂纹焊缝的有效方法。
The influence of the main process parameters on the bulging region of high-strength steel in narrow gap laser welding with filler wire was studied. By measuring the width ,W,max, of the weld bulging region and its distance d from the weld surface under different process conditions, the relationship between the main welding parameters and the bulging region size was established. The research results show that the ratio of the energy absorbed by the welding wire to the base metal is the main factor affecting the width and position of the bulging region. Reducing the laser power, increasing the welding speed and wire feeding can reduce the bulging region. The process range of different bulging angles ,β,<,30° and ,>,60° is further proposed, and reducing the bulging angle ,β, is an effective method to obtain solidification-free crack-free welds under the condition of large aspect ratio.
窄间隙激光填丝焊高强钢凝固裂纹鼓胀区
narrow gap laser weldinghigh-strength steelsolidification crackingbulging region
郝文魁, 刘智勇, 王显宗, 等. 舰艇用高强钢强度及其耐蚀性现状及发展趋势[J]. 装备环境工程, 2014(1):54-62.
Hao W K,Liu Z Y,Wang X Z,et al.Present Situation and Prospect of Studies on High Strength Steel and Corrosion Resistance in Naval Ship and Submarine[J]. Eq-uipment Environmental Engineering, 2014(1):54-62.
Czyryca E. J. Advances in High Strength Steel Technology for Naval Hull Construction[J]. Key Engineering Materials, 1993, 84-85:491-520.
Dong B, Cai X, Lin S, et al. Numerical Simulation on the Nonaxisymmetry Arc Characteristics in Narrow Gap TIG Welding: Responses to Welding Parameters[J]. The International Journal of Advanced Manufacturing Technology, 2021:2229-2242.
刘健, 贺智涛, 牛继承. 船用高强钢厚板窄间隙热丝TIG焊接工艺研究[J]. 材料开发与应用, 2018, 33(03):10-15.
Liu J,He Z T,Niu J C. Research on Narrow Gap Hot Wire TIG Welding of Thick Plate of High Strength Steel for Shipbuilding[J]. Development and Application of Materials,2018,33(03):10-15.
Liu G, Tang X, Han S, et al. Influence of Interwire Angle on Undercutting Formation and Arc Behavior in Pulsed Tandem Narrow-Gap GMAW[J]. Materials & Design, 2020, 193(6):108795.
余刚, 丁敏, 崔海超, 等. 10Ni5CrMoV钢旋转电弧窄间隙GMAW研究[J]. 焊接技术,2010,39(11):12-15.
Yu G,Ding M,Cui H C,et al. Study on rotation arc narrow gap gas metal arc welding of 10Ni5CrMoV steel[J]. Welding Technology,2010,39(11):12-15.
Holub, Luká, Dunovsky J, Kovanda K, et al. SAW-Narrow Gap Welding CrMoV Heat-resistant Steels Focusing to the Mechanical Properties Testing[J]. Procedia Engineering, 2015, 100:1640-1648.
张中元,聂帅强,王龙,等. 窄间隙埋弧焊在厚钢板拼接焊中的工艺研究[J]. 新技术新工艺,2019(09):31-33.
Zhang Z Y,Nie S Q,Wang L,et al. Research on Narrow-gap Submerged Arc Welding in Process of Thick Steel Plate Splicing[J]. New Technology & New Process,2019(09):31-33.
杨武雄, 信纪军, 方超, 等. 百毫米级304不锈钢超窄间隙激光焊接头的组织及性能[J]. 中国激光,2018,45(07):86-91.
Yang W X,Xin J J,Fang C,et al. Microstructures and Mechanical Properties of Hundred-Millimeter-Grade 304 Stainless Steel Joints by Ultra-Narrow Gap Laser Welding[J]. Chinese Journal of Lasers, 2018, 45(07):86-91.
孙清洁, 李军兆, 刘一搏. 大型厚壁构件窄间隙激光焊接研究现状[J]. 电焊机, 2020, 50(7): 9-17.
Sun Q J,Li J Z,Liu Y B. Research status of narrow gap laser welding for large thick-wall component[J]. Electric Welding Machine, 2020,50(7):9-17.
Smrr V, Amrutha P, Rashid R, et al. Narrow Gap Laser Welding (NGLW) of Structural Steels—a Technological Review and Future Research Recommendations[J]. International Journal of Advanced Manufacturing Technology, 2020, 111(7-8): 1-24.
Zhao Y, Ma S, Huang J, et al. Narrow-gap Laser Welding Using Filler Wire of Thick Steel Plates[J]. International Journal of Advanced Manufacturing Technology, 2017,93, 2955-2962.
Tsukamoto T , Kawanaka H , Maeda Y . Laser Narrow Gap Welding Of Thick Carbon Steels Using High Brightness Laser With Beam Oscillation[C]// 2011:141-146.
曹浩. 大厚度高强钢板窄间隙激光摆动填丝焊接工艺研究[D]. 北京: 机械科学研究总院, 2019.
Cao H.Narrow Gap Scanned Laser Welding with Filling Wire for Thick High-Strength Steel[D]. Beijing:China Academy of Machinery Science and Technology,2019.
Kannengiesser T , Boellinghaus T. Hot cracking tests—an overview of present technologies and applications[J]. Welding in the World, 2013, 57(1): 3-37.
Rappaz M ,Drezet J M ,Gremaud M.A new hot-tear-ing criterion[J]. Metallurgical and Materials Transactions A, 1999, 30(2): 449-455.
Aa A, Mb A, Xm A, et al. On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding-Science Direct[J]. Procedia CIRP, 2020, 94:5-10.
Moritz Oliver Gebhardt, Andrey Gumenyuk, Michael Rethmeier, et al. Numerical Analysis of Hot Cracking in Laser-Hybrid Welded Tubes[J]. Advances in Materials Science and Engineering,2013:520786.
Barbetta L D. Influence of Molten Pool Geometry and Process Parameters on Solidification Cracks formation in hybrid laser: GMA welding of thick API 5L X70 steel plates[J]. Master's thesis, 2014:80-81.
Phaoniam R. Evaluation and prediction method for solidification cracking during hot-wire laser welding with a narrow gap joint and GMAW process using computational simulation[D]. 広島大学 (Hiroshima University), 2014.
Phillips R. H, Metzbower E. A. Laser beam welding of HY80 and HY100 steels using hot welding wire addition[J]. welding journal, 1992, 71(6):201-208.
韩鹏薄,黄瑞生,李小宇,等. 高强钢激光焊接凝固裂纹研究现状[J]. 机械制造文摘:焊接分册,2022(3):20-26.
Han P B,Huang R S,Li X Y,et al. Research status of solidification cracks in laser welding of high-strength steel[J]. Welding Digest of Machinery Manufacturing,2022(3):20-26.
相关作者
相关机构