焊接参数对镀锌低碳钢板点焊接头抗剪切力的影响
Influences of Welding Parameters on the Shearing Strength of Resistance Spot-welded Joints of Galvanized Low Carbon Steel Sheets
- 2022年52卷第4期 页码:89-94
DOI: 10.7512/j.issn.1001-2303.2022.04.13
扫 描 看 全 文
扫 描 看 全 文
王丙旭,张宇,施泽平,等.焊接参数对镀锌低碳钢板点焊接头抗剪切力的影响[J].电焊机,2022,52(4):89-94.
WANG Bingxu, ZHANG Yu, SHI Zeping, et al.Influences of Welding Parameters on the Shearing Strength of Resistance Spot-welded Joints of Galvanized Low Carbon Steel Sheets[J].Electric Welding Machine, 2022, 52(4): 89-94.
通过正交试验法研究了焊接电流、焊接时间和电极压力对热浸镀锌低碳钢板点焊接头抗剪切力的影响规律,并分析最佳焊接工艺参数下点焊接头的微观组织、硬度分布和抗剪切力。结果表明,焊接电流对点焊接头抗剪切力影响最大,最佳焊接工艺参数为:焊接电流13 kA、焊接时间80 ms、电极压力4 kN,在该参数下点焊接头抗剪切力为8.637 kN,熔合区组织主要为板条状马氏体,硬度为320 HV,母材区组织主要为铁素体,硬度为102 HV,热影响区组织为板条状马氏体和铁素体,硬度介于熔合区和母材区之间。
The influences of welding parameters including welding current, welding duration and electrode force on the shearing strength of resistance spot-welded joints of hot-dipped galvanized low carbon steel sheets were studied by using orthogonal tests, and the microstructure, hardness distribution and shearing strength of welded joints produced by optimal welding parameters were also investigated. The results showe that the welding current has the most significant influences on the shearing strength of welded joints. The optimal welding parameters are welding current of 13 kA, welding duration of 80 ms and electrode force of 4 kN. The microstructure of welding zone is mainly lath martensite with hardness of 320 HV, the microstructure of substrate is mainly ferrite with hardness of 102 HV, the microstructure of heat affected zone is martensite and ferrite with the medium hardness.
电阻点焊镀锌低碳钢板焊接参数抗剪切力
resistance spot weldinggalvanized low-carbon steel sheetswelding parametersshearing strength
张仁坤, 程红红, 吴跃斌, 等. 输电铁塔用镀锌钢在不同浓度NaCl和NaHSO3中的腐蚀行为[J]. 腐蚀科学与防护技术,2018, 30(6): 585-593.
Zhang R K, Cheng H H, Wu Y B, et al. Corrosion behavior of galvanized steel for power transmission tower in solutions with different concentrations of NaCl and NaHSO3[J]. Corrosion Science and Protection Technology, 2018, 30(6): 585-593.
Liang T, Yuan H, Li C, et al. Corrosion inhibition effect of nano-SiO2 for galvanized steel superhydrophobic surface[J]. Surface and Coatings Technology,2021,
406: 126673.
原徐杰, 张俊喜, 张世明, 等. 镀锌层破损输电杆塔用镀锌钢在干湿交替作用下的腐蚀行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 395-399.
Yuan X J, Zhang J X, Zhang S M, et al. Corrosion behavior of galvanized steel for power transmission tower with breakage of zinc coating in polluted environment[J]. Journal of Chinese Society for Corrosion and Protection, 2013, 33(5): 395-399.
曹京宜, 方志刚, 李亮, 等. 国产镀锌钢管在不同水环境中的腐蚀行为: I淡水和盐水[J]. 中国腐蚀与防护学报, 2021, 41(2): 169-177.
Cao J Y, Fang Z G, Li L, et al. Corrosion behavior of domestic galvanized steel in different water environment: fresh water and salt water[J]. Journal of Chinese Society for Corrosion and Protection, 2021, 41(2): 169-177.
Valet S, Burkert A, Ebell G, et al. Determination of the corrosion product layer resistance on zinc and electrolytically galvanized steel samples by using gel electrolytes[J]. Electrochimica Acta, 2021(385): 138191.
王爱华, 朱久发. 国内外热镀锌板取代电镀锌板的发展趋势[J]. 钢铁研究,2007, 35(6): 53-55.
Wang A H, Zhu J F. Development trend of substituting hot-dip galvanized sheet for electro-galvanized sheet[J]. Research on Iron and Steel, 2007, 35(6): 53-55.
夏裕俊, 李永兵, 楼铭, 等. 电阻点焊质量监控技术研究进展与分析[J]. 中国机械工程, 2020, 31(1): 100-125.
Xia Y J, Li Y B, Lou M, et al. Recent advances and analysis of quality monitoring and control technologies for RSW[J]. China Mechanical Engineering, 2020, 31(1): 100-125.
Shen Y, Xia Y, Li H, et al. A novel expulsion control strategy with abnormal condition adaptability for resistance spot welding[J]. Journal of Manufacturing Science and Engineering, 2021, 143(11): 111009.
潘小强, 张立研, 曹艳艳, 等. 焊接时间对低碳钢点焊接头组织和性能的影响[J]. 热加工工艺, 2020, 49(21): 31-33.
Pan X Q, Zhang L Y, Cao Y Y, et al. Effect of welding time on structure and properties of low carbon steel spot welding joints[J]. Hot Working Technology, 2020,49(21): 31-33.
王鹏博, 张永强, 付参, 等. CP780镀锌复相钢板电阻点焊焊接特性[J]. 机械工程材料, 2021,45(5): 63-66,83.
Wang P B, Zhang Y Q, Fu C, et al. Resistance spot welding performance of CP780 galvanized complex-phase steel plate[J]. Materials for Mechanical Engineering, 2021, 45(5): 63-66,83.
周磊磊, 余腾义. 热镀锌DP780电阻点焊工艺研究[J]. 钢铁钒钛, 2017, 38(5): 152-156.
Zhou L L, Xu T Y. Research on spot welding process of hot galvanizing DP780[J]. Iron Steel Vanadium Titanium, 2017, 38(5): 152-156.
贺地求, 袁蒙, 赖瑞林. 马氏体钢与高强低合金钢电阻点焊组织结构演变分析[J]. 湖南大学学报(自然科学版), 2021, 48(4): 153-158.
He D Q, Yu M, Lai R L, et al. Analysis on microstructural evolution of resistance spot welding between martensitic steel and high-strength low-alloy steel[J]. Journal of Hunan University (Natural Sciences), 2021, 48(4): 153-158.
郑森, 程东海, 陈益平, 等. 镁合金/镀锌钢板电阻点焊接头拉剪断裂分析[J]. 焊接学报, 2017, 38(5): 104-107.
Zheng S, Cheng D H, Chen Y P, et al. Analysis of joint fracture of magnesium alloy and galvanized steel by resistance spot welding[J]. Transactions of the China Welding Institution, 2017, 38(5): 104-107.
编辑部网址:http://www.71dhj.comhttp://www.71dhj.com
相关作者
相关机构