Applicability Study of Welding Hot Tearing Criterion Involving Grain Boundary Effect

HAN Fang; WANG Yong; YANG Jing; ZHU Xiaoqing; WANG Han; ZHANG Zhihang; YANG Laishan; DONG Zhibo

doi:10.7512/j.issn.1001-2303.2024.08.10

Welding Virtual Simulation | Views : 0 下载量: 4 CSCD: 0

PDF
Export
Share
Collection
Album

Applicability Study of Welding Hot Tearing Criterion Involving Grain Boundary Effect
Vol. 54, Issue 8, Pages: 79-83(2024)
Published： 25 August 2024 ，
DOI： 10.7512/j.issn.1001-2303.2024.08.10
稿件说明：

扫描看全文

韩放，王勇，杨晶，等.晶界效应下的焊接热裂倾向判据适用性研究［J］.电焊机，2024，54（8）：79-83.

HAN Fang, WANG Yong, YANG Jing, et al.Applicability Study of Welding Hot Tearing Criterion Involving Grain Boundary Effect[J].Electric Welding Machine, 2024, 54(8): 79-83.
韩放，王勇，杨晶，等.晶界效应下的焊接热裂倾向判据适用性研究［J］.电焊机，2024，54（8）：79-83. DOI： 10.7512/j.issn.1001-2303.2024.08.10.

HAN Fang, WANG Yong, YANG Jing, et al.Applicability Study of Welding Hot Tearing Criterion Involving Grain Boundary Effect[J].Electric Welding Machine, 2024, 54(8): 79-83. DOI： 10.7512/j.issn.1001-2303.2024.08.10.

摘要

材料焊接热裂倾向评判在产品制造中具有重要作用，以往热裂倾向判据并未考虑晶界效应，故其适用性一直是讨论的热点问题。文中以Al-Cu合金为例，通过多晶凝固定量相场模型获取熔池凝固过程枝晶形貌，提取凝固路径。基于凝固路径开展了目前常用热裂倾向判据的适用性研究，包含RDG判据、Clyne-Davies判据和Sindo Kou判据。研究发现，RDG判据同实际焊接热裂倾向一致，且裂纹产生主要受孤立晶界段枝晶间压力降主导；Clyne-Davies判据及Sindo Kou判据评判由于计算过程忽略部分孤立晶界区间段，导致评判结果出现失真。通过对三个判据的研究，为材料热裂倾向评判提供了参考。

Abstract

The evaluation of hot cracking susceptibility in the welding of materials is important in the manufacture. In previous studies

the applicability of the hot tearing criteria has always been a hot issue because it did not consider the grain boundary effect. In this paper

taking Al-Cu alloy as an example

the dendrite morphology and solidified path were obtained by a quantitative phase field model of polycrystalline solidification. Based on the solidified path

the applicability of the widely-used hot tearing criteria was studied

including the RDG criterion

Clyne-Davies criterion

and Sindo Kou criterion. It is found that the RDG criterion is consistent with the actual welding hot cracking tendency

and the crack generation is mainly dominated by the pressure drop between dendrites in isolated grain boundary segments. The Clyne-Davies criterion and Sindo Kou criterion result in distortion because some isolated grain boundary intervals are ignored in the calculation process. Through the research of three criteria

a reference is provided for the evaluation of the hot cracking susceptibilities of materials.

关键词

热裂倾向凝固路径相场模型晶界效应

Keywords

hot cracking susceptibilitysolidification pathphase field modelgrain boundary effect

references

杨来山. 凝固全过程二元多相定量相场模型及Al-Cu合金热裂纹敏感性研究［D］. 黑龙江：哈尔滨工业大学，2021.

YANG L S. Quantitative binary and multi-phase Phase-field model of entire Solidification process and hot cracking susceptibility of Al-Cu alloy［D］. Heilongjiang： Harbin Institute of Technology，2021.

彭非，楚浩，杨兵. 5A06铝合金油箱氩弧焊热影响区裂纹分析及预防措施［J］. 电焊机，2007（07）：34-37.

PENG F，CHU H，YANG B. Analysis and prevention of fracture in 5A06 aluminum alloy fuel tank with manual TIG welding technology［J］. Electric Welding Machine，2007（07）：34-37.

张兆林. SA-213TP347HFG膜式水冷壁角焊缝热裂纹原因分析［J］. 电焊机，2021，51（12）：50-55.

ZHANG Z L. Analysis of hot cr ack in fillet weld of SA-213TP347HFG membrane water wall［J］. Electric Welding Machine，2021，51（12）：50-55.

YANG L S，Dong Z，Wang L，et al. Improved multi-order parameter and multi-component model of polycrystalline solidification［J］. Journal of Materials Science & Technology，2022，101（28）：217-225.

RAPPAZ M，DREZET J，GREMAUD M. A new hot-tearing criterion［J］. Metall Mater Trans A，1999，30：449-455.

YANG L S，YANG J，HAN F，et al. Hot cracking susceptibility prediction from quantitative multi-phase field simulations with grain boundary effects［J］. Acta Materialia，2023，250：118821.

WANG L，WANG N，PROVATAS N. Liquid channel segregation and morphology and their relation with hot cracking susceptibility during columnar growth in binary alloys［J］. Acta Materialia，2017，126：302-312.

KATGERMAN L. A mathematical model for hot cracking of aluminum alloys during D.C. casting［J］. Process Metallurgy，1982，34：46-49.

KOU S. A criterion for cracking during solidification［J］. Acta Materialia，2015，88：366-374.