Reason analysis and prevention measures on hot crack in butt weld of 12Cr1MoVG water wall tubes
Vol. 49, Issue 10, Pages: 92-96(2019)
DOI：

扫描看全文

XIAO Dongping, HUA Jinliang, GAO Miaomiao, et al. Reason analysis and prevention measures on hot crack in butt weld of 12Cr1MoVG water wall tubes. [J]. 49(10):92-96(2019)
DOI：

XIAO Dongping, HUA Jinliang, GAO Miaomiao, et al. Reason analysis and prevention measures on hot crack in butt weld of 12Cr1MoVG water wall tubes. [J]. 49(10):92-96(2019) DOI：

摘要

某12Cr1MoVG水冷壁部件在管屏对接焊后射线拍片时发现,部分对接焊缝存在横向缺陷显示。通过对缺陷样管进行化学成分、金相组织、断口和能谱分析,确定了缺陷性质为焊接热裂纹,产生于熔池金属凝固结晶过程。结合对相关焊接工艺和实际操作的调查,找出缺陷产生原因,并提出了预防措施。

Abstract

The transverse cracks were found in part of the butt welds of 12Cr1MoVG water wall panels after X ray inspection. By means of chemical composition analysis,microstructure examination,fracture and energy spectrum analysis,the nature of crack was identified as welding hot crack,which produced in the weld joint solidification. Combining with the investigation of relevant welding process and the actual operation,the causes of crack was found out and the prevention measures were put forward.

关键词

水冷壁管对接焊缝热裂纹

Keywords

water wall tubesbutt weldhot crack

references

Alert me when the article has been cited

提交

A Review of Test Methods for Evaluating on Liquation Cracking Susceptibility

³Cause Analysis and Preventive Measures of Weld Crack of 3 000 mPropylene Spherical Storage Tank