异质材料增材制造作为增材制造领域的一个前沿方向，通过一体化的结构功能设计，克服了单一材 料的性能局限，实现了传统单一材料无法达到的综合性能。本研究中，采用冷金属过渡电弧增材制造（CMT-WAAM）技术，利用高强钢（HSS）和低碳钢（LCS）焊丝，采用正交沉积策略制备了交叠层状异质金属（OLH）试样，成形良好且无明显冶金缺陷。HSS试样中主要为针状马氏体，LCS试样中主要为多边铁素体，而在OLH试样中，HSS区域主要为马氏体和部分铁素体，LCS区域主要为铁素体和部分马氏体。OLH试样中HSS区硬度约为340.7 HV，与HSS试样硬度（326.0 HV）接近，而LCS区硬度约为245.9 HV，相较于LCS试样硬度（171.1 HV）提高143.8%。OLH试样结合了HSS 试样的抗拉强度和 LCS 试样的延展性，拉伸性能介于HSS和LCS试样之间。
Heterogeneous materials additive manufacturing represents a cutting-edge direction in the additive manufacturing field. Its core significance lies in overcoming the performance limitations of single materials and achieving comprehensive properties unattainable with traditional materials through spatially integrated structural functional design. In this study
utilizing cold metal transfer wire arc additive manufacturing (CMT-WAAM) technology
samples of high-strength steel (HSS)
low-carbon steel (LCS)
and overlapping layered heterogeneous (OLH) were fabricated. Macroscopic and microscopic examinations revealed no significant defects. In the OLH samples
the HSS regions developed predominantly ferrite
while the LCS regions formed martensite. The HSS zones showed comparable hardness (340.7 HV) to monolithic HSS (326.0 HV). In contrast
the LCS zones exhibited a 143.8% increase in hardness (245.9 HV) compared to monolithic LCS (171.1 HV). The OLH samples combined HSS-grade tensile strength with LCS-level ductility.
DebRoy T ， Wei H L ， Zuback J S ， et al . Additive manufacturing of metallic components - Process，structure and properties ［J］. Progress in Materials Science ， 2018 ， 92 ： 112 - 224 .
Tan C ， Liu Y ， Weng F ， et al . Additive manufacturing of voxelized heterostructured materials with hierarchical phases ［J］. Additive Manufacturing ， 2022 ； 54 .
Gu G H ， Kim R E ， Kim E S ， et al . Fabrication of structural and compositional heterostructured CoCrNi-CoCrFeMnNi multi-material using direct energy deposition additive manufacturing ［J］. Intermetallics ， 2022 ，151：107726..
Li Y ， Su C ， Zhu J . Comprehensive review of wire arc additive manufacturing：Hardware system，physical process，monitoring，property characterization，application and future prospects ［J］. Results in Engineering ， 2022 ， 13 ： 100330 .
Zhou S ， Liu Z ， Yang G ， et al . Heterostructure microstructure and laves phase evolution mechanisms during inter-layer hammering hybrid directed energy deposition （DED） process ［J］. Materials Science and Engineering： A ， 2023 ， 886 ： 145668 .
Wang Y F ， Huang C X ， Wang M S ， et al . Quantifying the synergetic strengthening in gradient material ［J］. Scripta Materialia ， 2018 ； 150 ： 22 - 25 .
Ma H ， Zhao Y ， Lyu Z ， et al . What are the “dispersive shear bands” on the surfaces of layered heterostructured materials ［J］. Journal of the Mechanics and Physics of Solids ， 2023 ， 181 ： 105467 .
Ji W ， Zhou R ， Vivegananthan P ， et al . Recent progress in gradient-structured metals and alloys ［J］. Progress in Materials Science ， 2023 ， 140 ： 101194 .
Li J ， Zhang Q ， Huang R ， et al . Towards understanding the structure-property relationships of heterogeneous-structured materials ［J］. Scripta Materialia ， 2020 ， 186 ： 304 - 311 .
Wang Y ， Zhu Y ， Yu Z ， et al . Hetero-zone boundary affected region： A primary microstructural factor controlling extra work hardening in heterostructure ［J］. Acta Materialia ， 2022 ， 241 ： 118395 .
Guo S ， Li Y ， Duan M ， et al . Microstructure and mechanical properties of high nitrogen steel-high strength steel bimetallic multi-layered steels fabricated by plasma-arc additive manufacturing ［J］. Materials Today Communications ， 2023 ， 37 ： 107538 .
Jiang F ， Wang Y ， Yang Z ， et al . Mechanism of increased strength and ductility of martensite-austenite composite steel with different thickness ratios ［J］. Materials Science and Engineering：A ， 2022 ， 841 ： 143035 .
Li Z ， Liu Y ， Wang Y ， et al . Hierarchical strain band formation and mechanical behavior of a heterostructured dual-phase material ［J］. Journal of Materials Science & Technology ， 2023 ， 162 ： 25 - 37 .
Romero-Resendiz L ， El-Tahawy M ， Zhang T ， et al . Heterostructured stainless steel：Properties，current trends，and future perspectives ［J］. Materials Science and Engineering：R：Reports ， 2022 ， 150 ： 100691 .
Liu J ， Miao Y ， Wang Z ， et al . Improved strength in nickel-aluminum bronze/steel bimetallic component fabricated using arcing-wire arc additive manufacturing with alternating deposition strategy ［J］. Journal of Manufacturing Processes ， 2024 ， 111 ： 89 - 103 .
Liu F C ， Dong P ， Khan A S ， et al . Amorphous interfacial microstructure and high bonding strength in Al-Fe bimetallic components enabled by a large-area solid-state additive manufacturing technique ［J］. Journal of Materials Processing Technology ， 2022 ， 308 ： 117721 .
Liu K ， Yan Z ， Pan R ， et al . Interfacial bonding and microstructural evolution in Inconel-copper bimetallic structures fabricated by directed energy deposition-arc ［J］. Materials Science and Engineering： A ， 2024 ， 898 ： 146381 .
Cao R ， Yu G ， Chen J H ， et al . Cold metal transfer joining aluminum alloys-to-galvanized mild steel ［J］. Journal of Materials Processing Technology ， 2013 ， 213 （ 10 ）： 1753 - 1763 .
Zhang H ， Liu J . Microstructure characteristics and mechanical property of aluminum alloy/stainless steel lap joints fabricated by MIG welding-brazing process ［J］. Materials Science and Engineering：A ， 2011 ， 528 （ 19-20 ）： 6179 - 6185 .
Karim M A ， Jadhav S ， Kannan R ， et al . Investigating stainless steel/aluminum bimetallic structures fabricated by cold metal transfer （CMT）-based wire-arc directed energy deposition ［J］. Additive Manufacturing ， 2024 ， 81 ： 104015 .
Chen Y ， Zuo X ， Zhang W ， et al . Enhanced strength-ductility synergy of bimetallic laminated steel structure of 304 stainless steel and low-carbon steel fabricated by wire and arc additive manufacturing ［J］. Materials Science and Engineering： A ， 2022 ， 856 ： 143984 .
Chen M T ， Cai A ， Pandey M ， et al . Mechanical properties of high strength steels and weld metals at arctic low temperatures ［J］. Thin-walled structures ， 2023 ， 185 ： 110543 .
Ke K ， Xiong Y H ， Yam M C H ， et al . Shear lag effect on ultimate tensile capacity of high strength steel angles ［J］. Journal of Constructional Steel Research ， 2018 ， 145 ： 300 - 314 .
Zhang T ， Chen M T ， Cai A ， et al . Behaviour of high strength steel butt joints exposed to arctic low temperatures ［J］. Thin-Walled Structures ， 2023 ， 192 ： 111157 .
Zhou Z ， Chen Y ， Yam M C H ， et al . Experimental investigation of a high strength steel frame with curved knee braces subjected to extreme earthquakes ［J］. Thin-Walled Structures ， 2023 ， 185 ： 110596 .
Bhattacharya A ， Banaee S A ， Sharma M ， et al . IN718-LCS bi-metallic deposition by wire arc additive manufacturing：Issues，mitigation strategies，and interfacial behavior ［J］. Journal of Manufacturing Processes ， 2025 ， 140 ： 204 - 223 .
Huang H ， Zhang Z ， Jin X ， et al . Microstructure and mechanical properties of low-carbon high-strength steel fabricated by submerged arc additive manufacturing ［J］. Materials Today Communications ， 2025 ， 43 ： 111796 .
Badoniya P ， Srivastava M ， Jain P K . Microstructural Characteristics and Mechanical Performance of WAAM Fabricated LCS-SS 316L Bimetallic Structure Under Forced Cooling ［J］. Journal of Materials Engineering and Performance ， 2025 ： 1 - 15 .
Rafieazad M ， Nemani A V ， Ghaffari M ， et al . On Microstructure and Mechanical Properties of a Low-Carbon Low-Alloy Steel Block Fabricated by Wire Arc Additive Manufacturing ［J］. Journal of Materials Engineering and Performance ， 2021 ； 30 （ 7 ）： 4937 - 4945 .
Rodrigues T A ， Bairrão N ， Farias F W C ， et al . Steel-copper functionally graded material produced by twin-wire and arc additive manufacturing （T-WAAM） ［J］. Materials & Design ， 2022 ， 213 ： 110270 .
Ahsan M R U ， Tanvir A N M ， Ross T ， et al . Fabrication of bimetallic additively manufactured structure （BAMS） of low carbon steel and 316L austenitic stainless steel with wire + arc additive manufacturing ［J］. Rapid Prototyping Journal ， 2019 ， 26 （ 3 ）： 519 - 530 .
Raut LP ， Taiwade R V . Microstructure and Mechanical Properties of Wire Arc Additively Manufactured Bimetallic Structure of Austenitic Stainless Steel and Low Carbon Steel ［J］. Journal of Materials Engineering and Performance ， 2022 ， 31 （ 10 ）： 8531 - 8541 .
Wang C ， Liu T G ， Zhu P ， et al . Study on microstructure and tensile properties of 316L stainless steel fabricated by CMT wire and arc additive manufacturing ［J］. Materials Science and Engineering：A ， 2020 ， 796 ： 140006 .
Koseki T ， Inoue J ， Nambu S . Development of Multilayer Steels for Improved Combinations of High Stren-gth and High Ductility ［J］. Materials Transactions ， 2014 ， 55 （ 2 ）： 227 - 237 .
Spalek N ， Brunow J ， Braun M ， et al . WAAM Fabricated Laminated Metal Composites ［J］. Metals ， 2021 ， 11 （ 12 ）： 1948 .
相关作者
相关机构
公网安备11010802024621