Microstructure and Properties of High Frequency Pulse MIG Butt Joint for 6082 Aluminum Alloy Plate

FU Ningning; ZHOU Lujun; ZHU Xingxing; QU Zongqing; LIU Yuyang; WANG Wenchao; DING Chenggang; LI Songwei

doi:10.7512/j.issn.1001-2303.2023.11.08

Welding Technology | Views : 0 下载量: 12 CSCD: 0

PDF
Export
Share
Collection
Album

Microstructure and Properties of High Frequency Pulse MIG Butt Joint for 6082 Aluminum Alloy Plate
Vol. 53, Issue 11, Pages: 51-55(2023)
Received：07 August 2023，

Published：25 November 2023
DOI： 10.7512/j.issn.1001-2303.2023.11.08
稿件说明：

移动端阅览

付宁宁，周禄军，竺星星，等.6082铝合金中厚板高频脉冲MIG对接焊接头的组织和性能分析［J］.电焊机，2023，53（11）：51-55. DOI： 10.7512/j.issn.1001-2303.2023.11.08.

FU Ningning, ZHOU Lujun, ZHU Xingxing, et al.Microstructure and Properties of High Frequency Pulse MIG Butt Joint for 6082 Aluminum Alloy Plate[J].Electric Welding Machine, 2023, 53(11): 51-55. DOI： 10.7512/j.issn.1001-2303.2023.11.08.

摘要

采用高频脉冲MIG焊进行6082-T6铝合金15 mm中厚板对接焊，研究接头成形、微观组织和力学性能。接头条件为：坡口角度40°，焊接间隙1 mm，钝边0.5 mm，3层3道。结果表明：与常规脉冲MIG焊（深熔焊模式）相比，在相同的接头条件、焊接热输入降低约11%的状况下（常规脉冲MIG焊热输入为17.12 kJ/cm，高频脉冲MIG焊热输入为15.21 kJ/cm），高频脉冲MIG深熔焊的根部熔深增加约14%，两种焊接方法接头的组织类型相同，均为α-Al基体+化合物析出相，但常规脉冲MIG焊接头过热区的晶粒明显较为粗大；拉伸试样均断在热影响区处，断口呈典型的韧性断裂形貌，高频脉冲MIG接头的强度系数约为79%，较常规脉冲MIG焊接头的高出约4%；侧弯试样弯曲180°后，受拉面均无裂纹，焊接接头的塑性及熔合良好。对于6082-T6铝合金15 mm板厚的对接接头，高频脉冲MIG焊的焊接成形及接头的组织和性能优于常规脉冲MIG焊。

Abstract

In this paper

the appearance of weld

microstructure and mechanical properties of the butt joint 6082-T6 aluminum alloy (medium plate thickness is 15 mm) were investigated by high-frequency pulse MIG deep penetration welding( welding heat input

=15.21 kJ/cm).The joint conditions:groove angle 40 °

welding gap 1mm

thickness of root face 0.5 mm

3 layers and 3 runs . The research results showed that compared with conventional pulse MIG welding (deep penetration welding mode)

under the same joint conditions

less welding heat input ( for the conventional pulse MIG

=17.12 kJ/cm

high-frequency pulse MIG deep penetration welding

=15.21 kJ/cm

decreased by about 11%)

the root penetration of high-frequency pulse MIG deep penetration welding is increased about 14%. The microstructure types of the joints of the two welding methods were the same

both of which are α- Al matrix+compound precipitated phase

but the grain size in overheated zone of conventional pulse MIG welding was significantly coarser; The tensile specimens were all fractured in the heat affected zone

with typical ductile fracture morphology. The strength coefficient of high-frequency pulse MIG joints is about 79%

which was about 4% higher than that of conventional pulse MIG welded joints; After the side bending samples were bent 180 °

the tensile surface of SBB samples were all free of cracks

it showed that the plasticity of the welded joint is better

also the fusion of the welded joint. For the butt joint of 6082-T6 aluminum alloy medium plate (thickness 15mm)

the appearance of weld

microstructure and properties of high-frequency pulse MIG welding were superior to conventional pulse MIG welding.

关键词

Keywords

references

张子傲，张知航，黄继华，等 . 高速列车铝合金车体焊接工艺研究进展［J］. 轨道交通材料， 2023 ， 2 （ 01 ）： 1 - 7 .

ZHANG Z A ， ZHANG Z H ， HUANG J H ， et al . Advance in the Research of Welding Procedures for Aluminum Car Bodies of High Speed Train ［J］. Materials for Rail Transit ，， 2023 ， 2 （ 01 ）： 1 - 7 .

但龙 . 6XXX系铝合金车体型材粗晶的研究进展［J］. 轻合金加工技术， 2023 ， 51 （ 04 ）： 29 - 36 .

DAN L . Research on the coarse grain of 6××× series aluminum profile for rail vehicle body ［J］. Light Alloy Fabrication Technology ， 2023 ， 51 （ 04 ）： 29 - 36 .

Shi T Y ， Wang C M ， Mi G Y ， et al . A study of microstructure and mechanical properties of aluminum alloy using laser cleaning ［J］. Journal of Manufacturing Processes ， 2019 ， 42 ： 60 - 66 .

王宁 . 地铁铝合金车体的局部焊接结构可靠性研究［D］. 上海：上海应用技术大学， 2022 .

WANG N . Research on the Reliability of Local Welding Structure of Subway Aluminum Alloy Vehicle Body ［D］. Shanghai ： Shanghai University of Applied Technology ， 2022 .

郑长鑫，蔡明芳 . MIG焊接电流对6082铝合金薄板性能的影响［J］. 内燃机与配件， 2023 （ 09 ）： 73 - 75 .

ZHENG C X ， CAI M F . Effect of MIG Welding Current on Properties of 6082 Aluminum Alloy Thin Plate ［J］. Internal Combustion Engine & Parts ， 2023 （ 09 ）： 73 - 75 .

郭超超，丁成钢，杨大龙 . S355J2W+N耐候钢板根部大熔深MAG对接焊工艺及接头的组织和性能［J］. 电焊机， 2020 ， 50 （ 11 ）： 50 - 54 ．

GUO C C ， DINGC G ， YANGD L . Study on deep penetration root welding proce-dure，microstructure and mechanical properties of S355J2W+N weather-resistant steel MAG butt welded joint ［J］. Electric Welding Machine ， 2020 ， 50 （ 11 ）： 50 - 54 ．

李宋伟 . 地铁底架6082-T6铝合金中厚板MIG深熔焊工艺［D］. 辽宁：大连交通大学， 2023 .

LI S W . MIG deep penetration welding process for 6082-T6 aluminum alloy medium thick plate of subway underframe ［D］. Niaoning ： Dalian Jiaotong University ， 2023 ．

EN ISO 17639：2022 焊接接头的宏观和显微检验［S］. 2022 .

EN ISO 4136：2022 焊接接头的横向拉伸试验［S］. 2022 .

EN ISO 5173：2016 金属材料焊缝的有损检验-弯曲试验［S］. 2016 .

EN ISO 10042：2005 铝及其合金弧焊接头的缺陷评定组别［S］. 2005 .

EN ISO 15614-2：2005 铝及其合金弧焊工艺评定［S］. 2005 .

编辑部网址： http：//www.71dhj.com http://www.71dhj.com