Application and research of twin-electrode TIG cladding process on reactor pressure vessels manufacturing

ZOU Guowei; MA Peifeng; WANG Weibo; LI Zhijie; FANG Disheng

Views : 0 下载量: 774 CSCD: 4

PDF
Export
Share
Collection
Album

Application and research of twin-electrode TIG cladding process on reactor pressure vessels manufacturing
Vol. 49, Issue 4, Pages: 168-172(2019)
Published：2019
DOI：
稿件说明：

移动端阅览

DOI：

ZOU Guowei, MA Peifeng, WANG Weibo, et al. Application and research of twin-electrode TIG cladding process on reactor pressure vessels manufacturing[J]. Eletric Welding Machine2019, 49(4): 168-172. DOI：

摘要

按照核反应堆压力容器不锈钢堆焊工艺评定

分别堆焊了单钨极与双钨极不锈钢堆焊层

通过对比分析两者的焊缝成形、金相组织、硬度分布、化学成分、冲击性能、晶间腐蚀等

说明双钨极与单钨极的主要区别。结果表明

双钨极与单钨极堆焊均能获得良好的焊缝成形

但双钨极焊接效率较单钨极有大幅提升。双钨极与单钨极焊缝其金相组织、硬度分布、冲击性能和晶间腐蚀性能等较为接近。该技术已开始应用于反应堆压力容器的制造。

Abstract

According to reactor pressure vessel stainless steel cladding qualification

this paper conducted stainless steel cladding by single TIG and twin-electrode TIG

respectively. The main difference between double tungsten and single tungsten is illustrated by investigating and comparing the weld formation

metallographic structure

hardness distribution

chemical composition

impact properties and intergranular corrosion. Results show that both twin-electrode TIG and single TIG can produce excellent weld bead formation

but the efficiency of twin-electrode TIG cladding is much higher. And the weld bead properties produced by the two methods are similar.Twin-electrode TIG cladding process has been applied to the manufacture of reactor pressure vessels.